PrimaSelect Luvocom 3F PEKK 50082 - 1.75mm - 500g - Natural

PS-LUVO-3F

No ratings
Regular price€419,00
/
Tax included.

Weight
diameter
  • Low stock - 10 items left
  • Inventory on the way

Amazon.com: PrimaFIX Adhesive - Prevent Warping: Industrial & Scientific PrimaSELECT™ Luvocom 3F 9581 PEEK

PrimaSELECT ™ Luvocom 3F 9581 PEEK (polyetheretherketone) is a semi-crystalline thermoplastic that is one of the most commonly used high-performance plastics in the world. It is used to manufacture parts for the aerospace, gas, oil, medical and automotive industries.



Polyetherketone Ketone (PEKK) is a semi-crystalline thermoplastic from the polyaryletherketone family. With high heat resistance, chemical resistance, the ability to withstand high mechanical loads, is inherently flame retardant and has unique tribological properties .

PEKK filament has an adjustable crystallization rate that allows FFF or FDM users to take advantage of both the extreme performance of PAEKs and the easier processing of amorphous materials. PEKK filament is easier to print than regular PEEK filament with better layer adhesion and offers similar strength and durability properties. better dimensional stability. PEKK has a higher Tg than PEEK of 15 °C.

LUVOCOM® 3F PEKK 50082 was developed to outperform the standard PEKK materials available on the market. It features improved flow properties that improve printability and layer adhesion. This unique modified pure PEKK offers dimensional stability and is printable in unheated chambers, delivering semi-crystalline parts without distortion.

  • Specially optimized for industrial 3D printing

  • Isotropic shrink properties

  • Non-flammable (UL94 V-0)

  • Continuous operating temperature 255 ° C

  • Operating temperature 300 ° C (during the service life max. 200h)

  • Very chemically resistant

  • Low deformation

LUVOCOM® 3F PEKK 50082 material properties

  • Density 1.27 g / cm³
  • Tensile strength 90 MPa
  • Elongation at maximum force 5%
  • Modulus of elasticity 3 GPa
  • Bending strength 150 MPa
  • Elongation at max. force 6%
  • Flexural modulus 2.5 GPa

print settings

  • Printing temperature: 340 ° C (320-360 ° C)
  • Bed temperature: 110-140 ° C
  • Printing speed: 20-50mm/s
  • Drying instructions: 4 hours, 110 ° C
Community Verified icon



Material PEKK

  • Diameter 1.75mm
  • Tolerance ±0.05mm
  • Heated build platform required Yes, 110-140°C.
  • Printing temperature 340 ° C (320 - 360 ° C
  • Printing speed 20 - 50mm/s
  • Drying 4 hours, 110 ° C.
  • Filament weight 0.5 kg

  • Density 1.27 g / cm³
  • Tensile strength 90 MPa
  • Elongation at maximum force 5%
  • Modulus of elasticity 3 GPa
  • Bending strength 150 MPa
  • Elongation at max. force 6%
  • Flexural modulus 2.5 GPa