| flexural modulus | 1,882 - 2,385 MPa |
| flexural strength | 40-70Mpa |
| deformation temperature | 80℃ |
| thermal expansion | 95*E-6 |
| volume shrinkage | 3.72 - 4.24% |
| linear shrinkage | 1.05 - 1.35% |
| tensile strenght | 30 - 52Mpa |
| tensile modulus | 1,779 - 2,385 MPa |
| breaking strength | 130% |
| Hardness (Shore D) | 65 - 75D |
| glass transition temperature | 100℃ |
| density | 1.05-1.25g/cm3 |
| impact strength | 41-48 y/m |
| viscosity | 150-300MPa·s |
| curing time | 4 - 12s for slice thickness of 0.05 mm soil layer 40 - 60 s |