Polymaker PC-PBT Filament Natural 1,75mm 1000g - 3D Material-Shop
Polymaker PC-PBT Filament Natural 1,75mm 1000g - 3D Material-Shop
Polymaker PC-PBT Filament Natural 1,75mm 1000g - 3D Material-Shop

Polymaker PC-PBT Filament Natural 1.75mm 1000g

Art. Nr.: PM70260

No ratings
Regular price€58,90
/
Tax included.

Weight
Color
diameter
  • Low stock - 7 items left
  • Inventory on the way

Polymaker | PICCO's 3D World Shop Polymaker PC-PBT Filament

Improved mechanical properties for industrial quality components.

The Industrial range offers materials of high and technical quality. With the polymaker PC-PBT filament enables Polymaker to open up new possibilities for its users in 3D printing for new applications in a wide variety of industries.

Industrial products may require special equipment and skills.

Polymaker PC-PBT is a PC/PBT polymer blend that offers good heat resistance and toughness at low temperatures (-20˚C/-30˚C). Polymaker™ PC-PBT also exhibits excellent chemical resistance.

  • Diameter: 1.75mm
  • Quantity: 1000g
  • Colour: Natural

RECOMMENDED SETTINGS

  • Nozzle Temperature: 260˚C - 280˚C
  • Printing speed: 30 - 50mm/s
  • Bed Temperature: 100˚C - 115˚C
  • Chamber Temperature: 100˚C - 110˚C
  • Bed surface: Almost any surface with a thin layer of MAGIGOO PC
  • Cooling fan: OFF

MECHANICAL PROPERTIES

  • Modulus of elasticity: 1986 ± 85 (MPa)
  • Tensile strength: 41.8 ± 0.9 (MPa)
  • Bending strength: 64.4 ± 0.3 (MPa)
  • Charpy impact strength: 21.4 ± 3 (kJ/m2

THERMAL PROPERTIES

  • Glass transition temperature: 140˚C
  • Vicat softening point: 139˚C
  • Melting temperature: 223˚C

REMARKS

  • Drying settings: 80˚C for 8h
  • Recommended substrates: PolyDissolve™ S2

Miscellaneous:

When printing with Polymaker™ PC-PBT, we recommend using a heated chamber.
If a heated chamber is not used, it is recommended to anneal the printed part immediately after printing to relieve internal residual stress.
Annealing Settings: 90˚C for 2h

Application Notes

Technical data sheet

safety data sheet

You May Also Like


Recently viewed