Characteristics
- 1-component, UV-curing, 3D printing / 1-component, UV-curing, 3D-printing
- Fast hardening / fast curing
- High detail level
- tack free surfaces
- low viscosity
- Solvent-free
monomeric form
Monomer form (liquid) / monomer form (fluid): *
| resin / resin | DIN/EN/ISO standard | |
| Viscosity [mPa*s] | 150-200 | 2/r30 Brookfield |
| color | According to color selection / according selected color |
* Values are rounded results and may vary from batch to batch. / the results shown are rounded results
curing behavior
Depending on the printer type and variant, there are other programming parameters. If necessary, we recommend preparing a test object for use and checking any settings yourself.
According to which kind of printer other parameters are used. We recommend a test object to prove the parameters on your own.
| printer / printer | Coating thickness [μm] | Curing time / processing time [sec] |
| Burn in layers | 50 | 50 |
| NanoDLP | 50 | 5 |
For a defined post-curing we recommend a maximum of 5 minutes
polymeric form***
| Values | Properties /Data|Property | DIN/EN/ISO standard | |
| Shore A[HA] | 90 - 95 | ISO 7619 |
| Shore D[HD] | 50 - 60 | ISO 7619 |
| Young’s modulus / Young’s modulus [MPa] | 790 - 950 | EN ISO 178 |
| Flexural strength [MPa] | 32 – 37 | EN ISO 178 |
| Elongation at break / breaking point [%] | 5:4-6 | EN ISO 178 |
| Impact strength [kJ/m²] | 12 – 15.5 | ISO 179 |
| shrinkage [%] | 2 +/-1 | ISO 2577 |
| color | according to color selection / according selected color |
*** The values are rounded results without post-curing / the results shown are rounded results without post-curing